Carbon Fibre PET-G Composite

CARBON-P carbon fibre PET-G

CARBON-P is 20% carbon fibre reinforced PET-G based filament.

The resulting filament propertiy is a twice as stiff filament as our current PETG with increased impact and heat resistance (HDT) to 80˚C

CARBON-P suitable for a very wide variety of applications besides such as RC parts, drones, automotive and more.

Printing Temperature Range 225-245˚C

Does not require heated platform If available bed heat between 35-60c

Due to virtually no warping of CARBON-P the filament can also be printed without a heated bed.

With a heated bed the recommended temperature is ± 35-60˚C.

* Please consider the use of a hardened steel nozzle when printing with CARBONP as the carbon fibres are abrasive and will result in fast wear of regular brass nozzles.

CARBON-P can be used on all common desktop FDM or FFF technology 3D printers. Storage: Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.

A PET-G polymer filament which has been enfused with minute carbon fibres (reduced nozzle clogging).

Description

Specific gravity

Test method

ASTM D792

Typical Value

1,19 g/cc

MFI (300˚C -1,2kg)

ISO 1133

N.D

E-modulus 1mm/min

ISO 527

3800 MPa

Yield stress 50mm/min

ISO 527

52,5 MPa

Yield strain 50mm/min

ISO 527

4,2%

Strain at breakn50min/min

ISO 527

8,0%

Impact Strength
Izod Notched 23˚C

ISO 180-1A

3,8 kJ/m²